High Quality Submerged Arc Welding Flux for Stainless Steel

Aug 23, 2018


Product Detail

Basic Info

  • state:Solid

  • pH:Alkaline

  • Type:Inorganic

  • Melting Point:>600℃

  • Chemical Composition:CaF?>30%

  • Function:Protect Weld Metal

  • Application:Submerged-arc Welding

  • Manufacturing Method:Sintering

  • Alkalinity:About 1.8

  • Grain Size:2.0~0.28mm

  • OEM:Offered

  • Accompanied Wire:H0cr21ni10, H0cr19ni12m02, H1cr24ni13

  • Transport Package:25kg / Kraft Paper Bag. 40 Bags/Pallet

  • Origin:Weifang, Shandong, China

Product Description

High Quality Submerged Arc Welding Flux for Stainless Steel

High Quality Submerged Arc Welding Flux for Stainless Steel.jpg



Alkaline welding flux, it is agglomerated welding flux for stainless steel and heat resistance steel , alkalinity about 1.8 .It is gray and round grain size around 2.0-0.28mm . Yulin Brand agglomerated welding flux has very perfect mechanical properties of deposit metal , arc steady , nice weld formation , easy in slag removing .

According to : GB/T17854 F308-H0Cr21Ni10
                        F316-H0Cr19Ni12Mo2
                        F309-H1Cr24Ni13

Parameter introduction of  Submerged Arc Welding Flux for Stainless Steel

BrandAlkalinityClassificationGrain SizeGrain colorShape
YULINAbout 1.8Alkaline type2.0~0.28mmBlack and grayRound


Feature of  Submerged Arc Welding Flux for Stainless Steel
1: It can be operated with AC and DC .( The maximum welding current can reach 1200A )
2 It has strong anti stomata performance .
3: Steady arc ,nice welding appearance and easy in slag removing .
4:Deposit metal owns perfect mechanical properties .

Applications of  Submerged Arc Welding Flux for Stainless Steel
1:Accompanying suitable wires (H0Cr21Ni10 , H00Cr21Ni10, H00Cr19Ni12Mo2 ,etc .) .
2:Applied in welding of stainless steel and high alloy steel structures , etc . N
3:It has perfect mechanical properties of deposit metal .

Chemical Composition of Submerged Arc Welding Flux for Stainless Steel

SiO2 +TiO2CaO+MgOAl2O3 +MnOCaF2SP
5~106~1030~4040~50≤0.06≤0.08


Mechanical Properties of Submerged Arc Welding Flux for Stainless Steel

Accompanied  WiresYield Strength
(δ s) Mpa
Tensile Strength
(δ b ) Mpa
Elongation
A(δ 5) %
Charpy - V impact Test (J)
oC
20

H0Cr21Ni10
≥320480~650≥35≥75